Abstract
Thermal barrier coating (TBC) around film-cooling holes is a key failure location for turbine blade TBC. This study built a numerical model. The model used conjugate heat transfer (CHT) and sequential thermal-stress calculation methods. It analyzed the temperature and stress fields in the TBC around film-cooling holes. The holes had different inclination angles (30°, 45°, and 60°). It also explored the balance between cooling effectiveness and stress at these angles. Results show that increasing the film-cooling hole angle reduces the cooling film coverage area significantly. Cooling effectiveness becomes worse. The temperature field near the holes is complex. Sharp temperature gradients exist there. An inverse temperature gradient appeared in the top coat (TC) layer at the hole exit. Stress in the TBC was analyzed next. Analysis was conducted under rated operating conditions. Analysis was also completed after 500 h of creep under these conditions. Stress concentration around the holes is obvious. At room temperature, Mode I cracks easily form upstream of the holes. Mode II cracks easily form downstream. Under rated conditions, mixed-mode cracks (I + II) easily form downstream. The coating experiences larger stress at room temperature. This means that the coating is more likely to spall during cooling. Increasing the hole angle can reduce stress concentration. It can also lower the chance of crack formation. However, a larger angle increases the normal momentum of the cooling jet. This reduces film coverage. Therefore, after considering both cooling effectiveness and TBC failure, the 45° film-cooling hole is optimal.