Abstract
This paper investigates the effect of plasticity ball burnishing on characteristics of surface integrity, residual stress and hardness of laser direct energy deposited (DEDed) Stellite 21 alloys, with a focus on the burnishing directional effect on surface and microstructural deformation. The results demonstrated that the burnishing improved surface finish, reducing Sa and Sz by 24% and 47%, respectively. The burnishing flattened and modified the cellular/columnar grains at a depth of 50 µm, with the most notable changes observed on the cross-sectional plane normal to the burnishing direction. Compared to the ground surface, the burnishing introduced higher and deeper compressive stresses along normal to the burnishing/grinding direction (-1341 MPa and 61 µm) as compared to that along the burnishing direction (-449 MPa and 56 µm). Likewise, the burnishing increased the full width at half maximum (FWHM) in the same fashion by broadening XRD peaks along normal to the burnishing direction. Due to higher grain modification and dislocation density, the burnishing has improved microhardness at a depth of 320 µm by 26% along normal to the burnishing direction. These findings demonstrate that the plasticity ball burnishing has a directional effect on plastic deformation and can be considered a plausible technique for tailored surface integrity, residual stress and hardness, which potentially improve the service performance of DEDed Stellite 21 alloy components.