Abstract
A composite meeting the UL94 V-0 rating was produced by adding 30 wt% epoxy silane-modified aluminum trihydrate (EPATH) to a 60/40 epoxy/benzoxazine matrix. Various bimodal and trimodal composites containing 20-40 wt% of three types of ceramic fillers, i.e., aluminum oxide (Al(2)O(3)), boron nitride (BN), and magnesium oxide (MgO), were prepared to simultaneously achieve flame-retardant and thermal conductive properties. The bimodal composites with 40 wt% of Al(2)O(3) and MgO exhibited thermal conductivities of 1.22 W/m∙K and 1.29 W/m∙K, respectively, which were superior to that of the composite containing the same amount of ATH (1.0 W/m∙K). In contrast, both the coefficient of thermal expansion (CTE) and shear strength decreased with increasing ceramic filler content. For agglomerated BN, the filler loading was constrained above 30 wt% because its high specific volume caused a significant rise in the viscosity. In the trimodal composites with a total filler content of 40 wt% of Al(2)O(3) and BN, a BN fraction of 7.5 wt% yielded the highest thermal conductivity of 1.64 W/m∙K and the lowest water absorption of 0.69%. When the trimodal composites were exposed to -55 °C and 150 °C for 1000 h, they exhibited a reduction in shear strength of less than 30% compared to their initial values.