Abstract
The use of construction and demolition waste (CDW) as an alternative binder to ordinary Portland cement presents a promising solution through alkaline activation. This study evaluates the physical, mechanical, and microstructural behaviour of pastes and mortars produced with CDW-specifically concrete (RH) and ceramic (RC) waste-activated with NaOH and Na(2)SiO(3) (SS) solutions. Mortars were prepared with NaOH/SS ratios of 0.2 and 0.3 and an activator-to-precursor (AA/P) ratio of 0.2. Results showed that higher NaOH content accelerated alkaline activation, reducing setting times from 6.2 h to 3.7 h for RC and from 4.6 h to 3.2 h for RH. Conversely, increasing Na(2)SiO(3) content led to greater drying shrinkage, from -0.42% to -0.49% in RC and from -0.46% to -0.52% in RH. Compressive strength values at 28 days ranged from 7.6 to 8.2 MPa. X-ray diffraction (XRD) revealed the presence of non-reactive crystalline phases in both precursors, while Fourier transform infrared (FTIR) spectroscopy indicated the formation of CASH, CSH, and/or (N)CASH gels. This study highlights the potential of CDW as a sustainable alternative binder and the usefulness of the proposed method for optimising alkali-activated systems, contributing to circular economy strategies in the construction sector.