Abstract
Sheep wool is a low-value agricultural by-product with potential to contribute to more sustainable cementitious materials. This study investigates Segureña sheep wool fibres as reinforcement in cement mortars, comparing washed wool (W) and cement-encapsulated wool (E) at the same oven-dry raw wool dosages (0.5, 1.0, and 3.0 g per batch), and benchmarking against polypropylene (PP) fibres. Flexural and compressive strength were evaluated at 1, 7, and 28 days, whereas apparent density, water absorption, and thermal conductivity were assessed at 28 days. An intermediate dosage (1.0 g per batch) provided the most favourable mechanical response, while the highest dosage (3.0 g per batch) reduced performance, plausibly due to dispersion limitations and void formation. At 28 days, W-1 reached 9.65 ± 0.50 MPa in flexure (very close to PP-1) and 59.70 ± 1.05 MPa in compression, exceeding PP-1 in compression. Wool incorporation also reduced apparent density and yielded an observed reduction in thermal conductivity of up to ~18% at the highest dosage (single specimen per series). Overall, optimally dosed washed wool can deliver competitive mechanical performance while improving thermal behaviour, supporting circular-economy valorisation of waste wool in eco-mortars.