Abstract
The inhibition of recrystallization in high-strain nickel-based single-crystal superalloys remains a critical challenge for advanced turbine blade applications. This study investigates the evolution of the primary γ' phase and dislocation during annealing in a third-generation Re-containing single-crystal superalloy (WZ30) subjected to 5% compressive deformation. Isochronal annealing (700 to 1200 °C, 1 min) combined with scanning electron microscopy (SEM) and an electron backscatter diffraction (EBSD) analysis revealed a nonlinear variation of the geometrically necessary dislocation (GND) density, which reached a minimum of 1000 °C with 62.7% of the primary γ' phase retained. Prolonged recovery annealing at 1000 °C for 10 h effectively inhibited recrystallization during subsequent solution heat treatment. This result provides a practical strategy for inhibiting recrystallization in single-crystal superalloys.