Abstract
Sulfonated aromatic polymers (SAPs) represent promising alternatives to perfluorinated ionomers for proton-exchange membrane fuel cells (PEMFCs), but their high hydrophilicity and limited chemical stability often require structural reinforcement and controlled cross-linking. In this study, composite membranes based on sulfonated poly(phenylsulfone) (SPPSU) and sulfonated poly(ethersulfone) (SPES) were fabricated with and without electrospun PPSU nanofiber mats and subsequently cross-linked through a solvent-induced sulfone-bridge formation at 180 °C. SPPSU/SPES blends (70/30, 50/50, 30/70) displayed good miscibility, while PPSU fibers improved dimensional stability and suppressed excessive swelling. Cross-linking strongly influenced membrane properties: intermediate treatment (20 h) enhanced mechanical strength and solvent resistance with limited loss of IEC, whereas extended treatment (30 h) produced highly stable, low-swelling networks. Despite lower IEC and water uptake, 30 h-treated membranes exhibited higher proton conductivity, attributed to reduced tortuosity and more continuous ionic pathways. Mechanical and hydration analyses identified SPPSU-50, SPPSU-70, and SPPSU-100 as the most balanced compositions. Proton mobility analysis revealed high membrane tortuosity, consistent with dense cross-linked structures reinforced by fibers. Overall, the combined use of SPPSU/SPES blending, PPSU nanofiber reinforcement, and sulfone-bridge cross-linking yields robust, water-insoluble membranes with improved electrochemical performance suitable for PEMFCs and other applications.