Abstract
Nickel-Aluminum-Bronze (NAB) has gained significant attention in marine applications due to its excellent corrosion resistance and has shown growing potential for laser powder bed fusion (L-PBF) additive manufacturing. However, research on the fabrication of NAB alloys using L-PBF remains relatively limited. In this study, fully dense NAB samples were successfully fabricated through L-PBF process parameter optimization. The microstructural evolution and mechanical properties of both as-built and annealed L-PBF samples were systematically investigated and compared with those of traditionally cast NAB. The results reveal that the as-built L-PBF specimens primarily consist of columnar β' grains, with the α phase distributed along the grain boundaries and a small amount of κ phase precipitated within the β' matrix, distinctly different from the cast microstructure characterized by a columnar α-phase matrix with precipitated β' and κ phases. After annealing at 675 °C for 6 h, the β' phase in both methods decomposed into α + κ phases, and the original columnar structure in the L-PBF specimens transformed into a dendritic morphology. Compared to the cast samples, the L-PBF-produced NAB alloy exhibited significantly enhanced yield strength, tensile strength, and microhardness, attributable to rapid solidification during the L-PBF process. Following annealing, the yield strength and elongation increased by 12.8% and 184.4%, respectively, compared to the as-built condition, resulting from the decomposition of the martensitic phase into α + κ phases and further grain refinement.