Abstract
Supercapacitors, with their remarkable attributes such as including a high power density, an extended cycle life, and inherent safety, have emerged as a major research area for electrochemical energy storage. In this paper, phenylenediamine and glyoxal were used as raw material to prepare p-phenylenediamine glyoxal (PGo) with one single step. p-phenylenediamine glyoxal-ferrocene (PGo-Fc(x), x = 1, 0.3, 0.2, 0.1) composites were synthesized based on a poly-Schiff base. FTIR and XRD results indicated that ferrocene doping preserves the intrinsic PGo framework while inducing grain refinement, as evidenced by the narrowing of the XRD diffraction peaks. SEM observations further revealed distinct morphological evolution. CV (cyclic voltammetry), EIS (electrochemical impedance spectroscopy), and GCD (galvanostatic charge-discharge) were conducted on PGo-Fc(x) in order to examine its electrochemical performance. The PGo-Fc(0.3) in PGo-Fc(x) electrode material had a specific capacitance of 59.6 F/g at a current density of 0.5 A/g and 36 F/g at a current density of 10 A/g. Notably, even after undergoing 5000 charging-discharging cycles at 10 A/g, the material retained 76.2% of its specific capacitance compared to the initial cycle. Therefore, taking conductive polymers and metal oxide materials for modification can improve the stability and electrochemical performance of supercapacitors.