Abstract
This study examines the thermal performance of phase change material (PCM)-metal foam composites under base heating, a configuration more relevant to compact thermal energy storage (TES) and electronics-cooling applications, compared to the widely studied side-heated case. Metal foams with pore densities of 10, 20, and 40 PPI, but identical porosity (volumetric value), were impregnated with two PCMs (paraffin RT55 and RT64HC) and tested under varying heat fluxes. The thermophysical properties of three PCMs (RT42, RT55, and RT64HC) were first characterized using the T-history method. A control case consisting of pure PCM revealed significant thermal lag between the heater and the PCM, whereas the inclusion of a metal foam improved temperature uniformity and accelerated melting. The results showed that PPI variation had little influence on melting completion time, while PCM type, viz., melting temperature, strongly affected duration. Heat flux was the dominant parameter: higher input power substantially reduced melting times, although diminishing returns were observed at elevated heat fluxes. An empirical correlation from the literature, originally developed for side-heated foams, was applied to the base-heated configuration and reproduced the main melting trends, though it consistently underpredicted completion times at high fluxes. Overall, embedding PCMs in metal foams enhances heat transfer, mitigates localized overheating, and enables more compact and efficient TES systems. Future work should focus on developing correlations for non-adiabatic cases, exploring advanced foam architecture, and scaling the approach for practical energy storage and cooling applications.