Abstract
A mechanically robust flexible transparent conductor with high thermal and chemical stability was fabricated from welded silver nanowire networks (w-Ag-NWs) sandwiched between multilayer graphene (MLG) and polyimide (PI) films. By modifying the gas flow dynamics and surface chemistry of the Cu surface during graphene growth, a highly crystalline and uniform MLG film was obtained on the Cu foil, which was then directly coated on the Ag-NW networks to serve as a barrier material. It was found that the highly crystalline layers in the MLG film compensate for structural defects, thus forming a perfect barrier film to shield Ag NWs from oxidation and sulfurization. MLG/w-Ag-NW composites were then embedded into the surface of a transparent and colorless PI thin film by spin-coating. This allowed the MLG/w-Ag-NW/PI composite to retain its original structural integrity due to the intrinsic physical and chemical properties of PI, which also served effectively as a binder. In view of its unique sandwich structure and the chemical welding of the Ag NWs, the flexible substrate-cum-electrode had an average sheet resistance of ≈34 Ω/sq and a transmittance of ≈91% in the visible range, and also showed excellent stability against high-temperature annealing and sulfurization.