Abstract
This investigation evaluates the viscosity and flow performance of cationic polyacrylamide (CPAA) solutions by assessing the effect of CPAA concentrations, shear rate, temperature, and electrolyte salt types. The study aims to characterize the flow behavior of CPAA solutions for different industrial utilizations under some challenging conditions of high salinity of two different electrolytes and high-temperature environments. In addition, the study addresses the critical shear rate thresholds at which the transition from shear-thinning to shear-thickening occurs. An Anton Paar rotational rheometer was employed to evaluate the flow behavior of cationic polyacrylamide solutions over the range of 20-80 °C at 20 °C intervals. Polymer samples were prepared from CPAA powder in a concentration range of 500-5000 ppm. To determine the electrolyte effects, NaCl and CaCl(2) were incorporated into the polymer solutions with a concentration range of 0-10 Wt.%. This study revealed that shear stress is vastly sensitive to CPAA concentration at shear rates less than 200 s(-1), whereas this sensitivity reduces at higher shear rates where the resulting profiles converge. Moreover, a considerable decrease in shear stress was reported with temperature as a result of the thermal influence on the molecular interaction forces. Rheological analysis of the CPAA solutions shows they exhibit strong non-Newtonian shear-thinning behaviors with viscosity decreasing significantly as the shear rate approaches 200 s(-1). On the contrary, a transition to a shear-thickening profile is observed at a shear rate above this limit of 200 s(-1). The results show that the dynamic viscosity of the CPAA solutions rises significantly as the concentration increases from 500 to 5000 ppm. At a shear rate of 10 s(-1), the dynamic viscosity increased from 2.4 to 33.8 mPa·s as the CPAA concentration increased from 500 to 5000 ppm (exactly 2.4, 11.8, 16.6, and 33.8 mPa.s for 500, 1500, 2500, and 5000 ppm, respectively). Additionally, increasing the temperature from 20 to 80 °C exerts a strong negative influence on dynamic viscosity. Specifically, for the 5000 ppm concentration at a shear rate of 10 s(-1), the dynamic viscosity decreased from 33.8 to 18.3 mPa.s as the temperatures rose from 20 to 80 °C (recorded as 33.8, 27.9, and 18.3 mPa.s at 20, 40, and 80 °C, respectively). Furthermore, the introduction of different electrolytes, such as NaCl and CaCl(2), significantly reduces the viscosity flow profiles.