Abstract
Microbial Induced Carbonate Precipitation (MICP) is regarded as a promising eco-friendly alternative to traditional Portland cement for soil stabilization. However, the feasibility of applying bio-cemented soil as a road base material remains inadequately studied, particularly in terms of the relationships between MICP treatment parameters-such as solution content, curing age, and the ratio of bacterial solution (BS) to cementation solution (CS) -and key mechanical and durability properties under realistic road conditions. In this study, an optimal curing condition for bio-cemented sand was first determined through unconfined compression strength (UCS) tests and calcium carbonate content (CCC) determination. Subsequently, dynamic triaxial tests were conducted to evaluate its resistance to cyclic loading. Further road performance tests, including splitting tensile strength, freeze-thaw resistance, temperature shrinkage, and arch expansion assessments, were carried out to comprehensively evaluate the material's applicability. Scanning electron microscopy (SEM) was employed to elucidate the microstructural mechanisms underlying strength development. The results show that the strength (4.28 MPa) of bio-cemented sand cured under optimal conditions (12% bio-cured solution content, a BS-to-CS ratio of 1:4 and 7-d curing age) satisfies the criteria for road base applications. MICP treatment significantly improved the dynamic properties of aeolian sand (AS), reducing the cumulative plastic axial strain (ε(p)) by nearly 11-46% and increasing the dynamic elastic modulus (E(d)) by approximately 7-31% compared to untreated sand. The material also demonstrates satisfactory performance across all four road performance metrics. Microstructural analysis reveals enhanced interparticle bonding due to calcium carbonate precipitation, with samples prepared near the optimum moisture content exhibiting superior integrity and strength. Overall, bio-cemented sand demonstrates excellent potential as a sustainable road base material. These findings provide a theoretical foundation for practical applications of similar bio-cemented soils in road engineering.