Abstract
The particularities of cesium incorporation into synthetic calcium phosphates with either apatite or whitlockite-type structures were investigated using the sorption process from aqueous solution and further heating to 700 °C. The nanoparticles for sorption were prepared by wet precipitation from aqueous solutions at a fixed molar ratio of Ca/P = 1.67 and two different ratios of CO(3)(2-)/PO(4)(3-) (0 or 1). The obtained substituted calcium phosphates and corresponding samples after the sorption of cesium from solutions with different molar concentrations (c(Cs(+)) = 0.05, 0.1 and 0.25 mol L(-1)) were characterized by powder X-ray diffraction, FTIR spectroscopy, scanning electron microscopy and elemental analysis. Based on the combination of X-ray diffraction and elemental analyses data for the powders after sorption, the cesium incorporated in the apatite- or whitlockite-type structures and its amount increased with its concentration in the initial solution. For sodium-containing calcium phosphate even minor content of Cs(+) in its composition significantly changed the general principle of its transformation under annealing at 700 °C with the formation of a mixture of α-Ca(3)(PO(4))(2) and cesium-containing apatite-related phase. The obtained results indicate the perspective of using of complex substituted calcium phosphates nanoparticles for immobilization of cesium in the stable whitlockite- or apatite-type crystal materials.