Abstract
AIM: The aim of this study was to evaluate the effect of proanthocyanidin and C. sinensis-polyphenols on microtensile bonding properties of prepared teeth with resin-modified glass ionomer cement (GIC). SETTING AND DESIGN: This was an in vitro study. MATERIALS AND METHODS: Seventy-eight maxillary premolars were selected and mounted into auto-polymerizing acrylic resin blocks. The samples were prepared and metal crowns were fabricated. The samples were randomly divided into three groups. Samples under Group 1 were not treated with any of the extracts and followed conventional bonding protocol. Samples under Group 2 and Group 3 were treated with proanthocyanidin and C. sinensis-polyphenols, respectively. After dentin treatment, these samples were luted to metal crowns using resin-modified GIC. Universal testing machine was used to measure the load at which the crowns were debonded and microtensile bond strength in MPa was calculated. STATISTICAL ANALYSIS: The results were statistically analyzed using one-way ANOVA and post hoc Tukey HSD. RESULTS: Samples treated with C. sinensis polyphenols (Group 3) had maximum bond strength followed by Group 2, where the samples were treated with proanthocyanidin. CONCLUSION: C. sinensis polyphenols due to their anti-proteolytic and antioxidant properties showed improved bond strength compared to proanthocyanidin, a cross-linking agent, followed by conventional bonding protocol.