Abstract
Flame-retardant poly (ethylene terephthalate) composites (FR PET) have been developed with the potential to be used as substrates in applications where flexibility and transparency are required. Several phosphorous-based flame retardants of a different nature were selected here for compounding by melt blending with a low-molecular-weight PET polymer. The fire reaction, transparency, and mechanical properties were analyzed. TGA and cone calorimetry were used to elucidate the gas-phase and condensed-phase actions of flame retardants and their effectivity. Cone calorimeters showed an improved performance with the addition of flame retardants, particularly a reduction in generated heat, improving the FGI (fire growth index) value. However, a V0 classification (following the UL94 standard) was achieved only with the addition of an organic phosphonate, Aflammit PCO900, to the PET matrix. This behavior was linked to the early reaction of this flame retardant in the gas phase, in addition to a plastification effect that causes the removal of the polymer from the incident flame. The presence of flame retardants reduced the transparency of composites over the neat PET, but, nevertheless, a good optical performance remained. No special effect was observed on the crystallization parameters. Therefore, the increase in opacity can be attributed to the poor miscibility of flame retardants and/or differences in the diffraction index of the polymer and FR additives.