Abstract
The main purpose of this study is to prepare a melamine aniline formaldehyde foam, an MAF copolymer, with lower water sensitivity and non-flammability properties obtained by the condensation reaction of melamine, aniline, and formaldehyde. In addition, the preparation of MAFF composites with organoclay reinforcement was determined as a secondary target in order to obtain better mechanical strength, heat, and sound insulation properties. For the synthesis of foams, the microwave irradiation technique, which offers advantages such as faster reactions, high yields and purities, and reduced curing times, was used together with the heating technique and the effect of organoclay content on the structural and textural properties of foams and both heat insulation and mechanical stability was investigated. Virgin melamine formaldehyde foam, MFF, melamine aniline formaldehyde foam, MAFFF, and melamine aniline formaldehyde-organoclay nanocomposite foams prepared with various organoclay contents, MAFOCFs, were characterized by HRTEM, FTIR, SEM, and XRD techniques. From spectroscopic and microscopic analyses, it was observed that organoclay flakes could be exfoliated without much change in the resin matrix with increasing clay content. In addition, it was determined that aniline formaldehyde, which is thought to enter the main polymer network as a bridge, caused textural changes in the polymeric matrix, and organoclay reinforcement also affected these changes. Although the highest compressive strength was obtained in MAFOCF5 foam with high organoclay content (0.40 MPa), it was determined that the compressive strengths in the nanocomposites were generally quite high despite their low bulk densities. In the prepared nanocomposite with 0.30% organoclay content (MAFOCF2), 0.33 MPa compressive strength and 0.051 thermal conductivity coefficient were measured. For virgin polymers and composites, bulk density, thermal conductivity, and compressive strength values were determined in the order of magnitude as MFF > MAFOCF1 > MAFOCF5 > MAFOCF6 > MAFF > MAFOCF3 > MAFOCF2 > MAFOCF4; MFF > MAFF > MAFOCF6 > MAFOCF5 > MAFOCF1 > MAFOCF4 > MAFOCF3 > MAFOCF2 and MAFOCF5 > MAFOCF4 > MAFOCF2 > MAFF > MAFOCF6 > MFF > MAFOCF1 > MAFOCF3. As a result, both compressive strength and thermal conductivity values indicate that nanocomposite foam with 0.20 wt% organoclay content can be a promising new insulation material.