Abstract
The high-speed sintering of zirconia has become essential for ceramic dental prosthesis treatment in a single visit. Previous studies have shown that 5 mol% yttria-stabilized zirconia (5Y zirconia), with the exception of some types, loses strength and translucency with high-speed sintering. In this study, 0.15-0.92 wt% Ga(2)O(3), which is expected to promote the sintering of zirconia, was added to improve the properties of 5Y zirconia high-speed sintered bodies, and the effect of its addition was evaluated. The specimens were characterized by density and translucency measurements, a three-point bending test, X-ray diffraction (XRD), scanning electron microscopy (SEM), and shrinkage measurement. The addition of Ga(2)O(3) improved both translucency and flexural strength of 5Y zirconia high-speed sintered bodies. XRD and SEM observations revealed that this improvement in properties was due to the change in the crystal phase composition and the decrease in the amount and size of pores due to the addition of Ga(2)O(3). Shrinkage measurements also revealed that the addition of Ga(2)O(3) changed the sintering behavior of 5Y zirconia, suggesting that this change led to a reduction in porosity. From the above results, it was concluded that Ga(2)O(3) addition is effective in improving the properties of 5Y zirconia high-speed sintered bodies.