Abstract
The alkali-free accelerator based on aluminum sulfate is widely used in shotcrete in tunnels. Long-term Ca-leaching of shotcrete may adversely affect the tunnels in a water-rich mountain. It is necessary to examine further the impact of the AS accelerator and w/c on cement hydration and leaching. In this study, all the cement pastes were cured in the environment with R.H. > 95% and 20 ± 1 °C for 60 days and leached in a running water test with 6 M NH(4)Cl at 1 cm/s. The hydration kinetics was characterized by isothermal calorimetry. Additionally, the microstructural and mineralogical alterations were characterized by XRD, SEM, MIP, and N(2) absorption. The results show that (1) the AS accelerator affected the hydration kinetics of cement by stimulating early hydration and delaying the late silicate hydration, resulting in AS-accelerated cement pastes with rougher pore structure. As a result, the higher the dose of AS accelerator, the faster the cement pastes will leach. (2) Hydration kinetics of the accelerated cement are not affected by the w/c. The AS-accelerated cement pastes with lower w/c have a denser pore structure. So, the reduction in the w/c contributes to leaching resistance.