Abstract
Although vacuum-deposited metal halide perovskite light-emitting diodes (PeLEDs) have great promise for use in large-area high-color-gamut displays, the efficiency of vacuum-sublimed PeLEDs currently lags that of solution-processed counterparts. In this study, highly efficient vacuum-deposited PeLEDs are prepared through a process of optimizing the stoichiometric ratio of the sublimed precursors under high vacuum and incorporating ultrathin under- and upper-layers for the perovskite emission layer (EML). In contrast to the situation in most vacuum-deposited organic light-emitting devices, the properties of these perovskite EMLs are highly influenced by the presence and nature of the upper- and presublimed materials, thereby allowing us to enhance the performance of the resulting devices. By eliminating Pb° formation and passivating defects in the perovskite EMLs, the PeLEDs achieve an outstanding external quantum efficiency (EQE) of 10.9% when applying a very smooth and flat geometry; it reaches an extraordinarily high value of 21.1% when integrating a light out-coupling structure, breaking through the 10% EQE milestone of vacuum-deposited PeLEDs.