Abstract
Diffusion bonding has many advantages, but it also has its specifics. When creating heterogeneous joints, problems arise with the creation of intermetallic phases. For this reason, an interlayer is needed to prevent the creation of these unfavorable phases. It is important to ensure that the interlayer is of sufficient thickness to prevent the elements from diffusing through the entire interlayer and the intermetallic phases from being formed again. Conversely, too thick an interlayer causes an increase in the heterogeneity of the bond properties. The creation of the initial diffusion bonds in a heterogeneous diffusion joint of AISI 304 and AISI 316L steel with a 0.2 mm thick nickel interlayer was made in a Gleeble 3500. The experiments to determine the diffusion kinetics were carried out in a vacuum furnace, with subsequent evaluation by EDX (Energy Dispersive X-ray Spectroscopy) analysis. Subsequently, the diffusion coefficients of nickel into both steels were determined, and generalized equations were formulated to calculate the diffusion coefficients for temperatures in the range of 950 to 1150 °C and holding times in the range of 3600 to 18,000 s. Equations are also given to determine the width of the diffused zone between each steel and the Ni interlayer.