Abstract
A diamond gel polishing disk with self-sharpening ability is proposed to solve the problem of glazing phenomenon in the gel polishing disks. Aluminum nitride (AlN) powder with silica sol film coating (A/S powder) is added to the polishing disk, and a specific solution is used to dissolve the A/S powder during polishing, forming a pore structure on the polishing disk. To realize the self-sharpening process, the dissolution property of the A/S powder is analyzed. The effect of A/S powder content on the friction and wear performance and the polishing performance of 4H-SiC wafers are investigated. Results showed that the friction coefficient of the polishing disk with 9 wt% A/S powder content is the most stable. The surface roughness R(a) of 2.25 nm can be achieved, and there is no obvious glazing phenomenon on the polishing disk after polishing. The surface roughness of the 4H-SiC wafer is reduced by 38.8% compared with that of the polishing disk with no A/S powder addition after rough polishing, and the 4H-SiC wafer then obtained a damage-free surface with a R(a) less than 0.4 nm after fine polishing by chemical mechanical polishing (CMP).