Abstract
Heteroepitaxial growth of high Al-content AlGaN often results in a high density of threading dislocations and surface hexagonal hillocks, which degrade the performance and reliability of AlGaN-based UVC light emitting diodes (LEDs). In this study, the degradation mechanism and impurity/defect behavior of UVC LEDs in relation to the hexagonal hillocks have been studied in detail. It was found that the early degradation of UVC LEDs is primarily caused by electron leakage. The prominent contribution of the hillock edges to the electron leakage is unambiguously evidenced by the transmission electron microscopy measurements, time-of-flight secondary ion mass spectrometry, and conductive atomic force microscopy. Dislocations bunching and segregation of impurities, including C, O, and Si, at the hillock edges are clearly observed, which facilitate the trap-assisted carrier tunneling in the multiple quantum wells and subsequent recombination in the p-AlGaN. This work sheds light on one possible degradation mechanism of AlGaN-based UVC LEDs.