Abstract
Magnesium and its alloys have been restricted in their industrial applications due to problems related to their formability. To overcome this issue, controlling the crystallographic texture is important, and the texture formation mechanism should be investigated in relation to factors including deformation conditions and solute atoms. In particular, the effects of solute atoms on the texture formation behavior should be further analyzed because they can considerably affect the deformation behavior. Thus, in this study, to clarify the effect of aluminum concentration on the texture formation behavior and microstructure, high-temperature uniaxial compression tests were conducted on three types of AZ-series magnesium alloys (AZ31, AZ61, and AZ91). Compression was conducted at 673 K and 723 K, with strain rates of 0.05 s(-1) and 0.005 s(-1), up to a true strain of -1.0. Cylindrical specimens were prepared from a rolled plate that had a (0001) basal texture and was compressed parallel to the c-axis of the grains. Consequently, work softening and fiber texture formation were observed in all the specimens. During the deformation, the development of grain boundaries, which is a typical characteristic of continuous dynamic recrystallization (CDRX), was observed, and the (0001) texture was highly developed with increasing Al content. Although each alloy was associated with the same deformation conditions and mechanisms, the AZ31 alloy exhibited a non-basal texture component. The stacking fault energy contributed to the generation of slip systems and gliding, and it was seen as the main reason for texture variation.