Abstract
Silicon is considered as the most promising anode material for high performance lithium-ion batteries due to its high theoretical specific capacity and low working potential. However, severe volume expansion problems existing during the process of (de)intercalation which seriously hinders its commercial progress. Binder can firmly adhere silicon and conductive agent to the current collector to maintain the integrity of the electrode structure, thereby effectively alleviating the silicon volume expansion and realizing lithium-ion batteries with high electrochemical performance. In this paper, citric acid (CA) and carboxymethyl cellulose (CMC) are adopted to construct a covalently crosslinked CA@CMC binder by an easy-to-scale-up esterification treatment. The Si@CA@CMC-1 electrode material shows an impressive initial coulombic efficiency (ICE) at 82.1% and after 510 cycles at 0.5 A/g, its specific capacity is still higher than commercial graphite. The excellent electrochemical performance of Si@CA@CMC-1 can be attributed to the ester bonds formed among CA@CMC binder and silicon particles. Importantly, by decoupling in situ EIS combining XPS at different cycles, it can be further proved that the CA@CMC binder can tune the component of SEI which provide a new-route to optimize the performance of silicon.