Abstract
Solid-state electrolytes (SSEs), particularly garnet-type Li(6.4)La(3)Zr(1.4)Ta(0.6)O(12) (LLZTO), offer high stability and a wide electrochemical window. However, their grain boundaries limit ionic conductivity, necessitating high-temperature sintering for improved performance. Yet, this process results in brittle electrolytes prone to fracture during manufacturing. To address these difficulties, solvent-free solid-state electrolytes with a polyacrylonitrile (PAN) coating on LLZTO particles are reported in this work. Most notably, the PAN-coated LLZTO (PAN@LLZTO) electrolyte demonstrates self-supporting characteristics, eliminating the need for high-temperature sintering. Importantly, the homogeneous polymeric PAN coating, synthesized via the described method, facilitates efficient Li(+) transport between LLZTO particles. This electrolyte not only achieves an ionic conductivity of up to 2.11 × 10(-3) S cm(-1) but also exhibits excellent interfacial compatibility with lithium. Furthermore, a lithium metal battery incorporating 3% PAN@LLZTO-3%PTFE as the solid-state electrolyte and LiFePO(4) as the cathode demonstrates a remarkable specific discharge capacity of 169 mAh g(-1) at 0.1 °C. The strategy of organic polymer-coated LLZTO provides the possibility of a green manufacturing process for preparing room-temperature sinter-free solid-state electrolytes, which shows significant cost-effectiveness.