Abstract
Nacre-inspired metal matrix composites have received much attention due to their excellent deformation coordination ability, which can achieve the synergy of strength and ductility. The preparation of nacre-like Al matrix composites by freeze casting has been a promising application, but the continuous ceramic-rich layer affects the corrosion resistance of the composites, facing complex corrosion problems during service. In this work, the microstructure and corrosion behavior of the nacre-inspired (TiBw-TiB(2))/Al composites fabricated by freeze casting and squeeze casting were systematically studied. The results indicated that the Al layers and ceramic-rich layers had little change, about 35 μm and 31 μm, respectively, with an increasing ratio of the Ti/TiB(2). Meanwhile, a high Ti/TiB(2) ratio resulted in an increase in the Fe-Ti intermetallic phases, which was detrimental to the corrosion performance of the composites and was prone to pitting. The electrochemical test results showed that the 3Ti7TiB(2) composite had the lowest corrosion current density (15.9 μA) and intergranular corrosion depth (231 μm), indicating that it had the best corrosion resistance, which can be attributable to its stable and dense passivation film. Two different corrosion phenomena during the intergranular corrosion test existed in the present nacre-inspired (TiBw-TiB(2))/Al composites: intergranular corrosion in the Al matrix layer and pitting corrosion in the ceramic-rich layer. Among all the composites, the corrosion depth of the 3Ti7TiB(2) composite was the smallest and significantly less than that of the 2024Al alloy. In addition, the continuous ceramic-rich layer acted as a corrosion channel during corrosion, significantly degrading the corrosion resistance of the nacre-like Al composites.