Abstract
The impact of grinding on particle size, thermal behaviour, and sintering ability of yttrium aluminate glass microspheres with eutectic composition (76.8 mol % Al(2)O(3) and 23.2 mol % Y(2)O(3)) was studied. The work was conducted with the aim of determining the optimal particle size and grinding conditions of glassy powder used for hot-pressing of ceramic and glass-ceramic materials with desired mechanical properties. The flame synthesis was used for the preparation of glass microspheres (diameter ∼ 40 μm). Ball milling procedure under different conditions was applied to adjust of size of prepared microbodies. The milled powders were subsequently hot pressed. The prepared samples (raw, milled microspheres and hot-press sintered bodies were characterised by X-ray powder diffraction, and scanning electron microscopy. Thermal analysis and particle size analysis in combination with X-ray powder diffraction and high temperature X-ray diffraction was used for detailed inspection of thermal behaviour and phase changes in raw and milled systems in the temperature interval 25-1200 °C. The samples after flame synthesis and after milling were found to be X-ray amorphous. The particle size measurements showed that the systems with a smaller average size D [0.9] ∼ 25 μm and a monomodal particle size distribution were prepared after 6h of milling. Thermal analysis in combination with X-ray and high temperature X-ray analysis indicated a difference in the crystallization mechanism of the yttrium aluminate garnet phase depending on the milling time. The bulk glass ceramic with fine lamellar eutectic microstructure and interesting mechanical properties (Vickers hardness H(V=)17.6 ± 0.2 GPa, indentation fracture toughness K(IC) = 4.3 ± 0.3 MPa.m(1/2)) resulted from the sintering of microspheres milled for 6h under the "gentlest" conditions (milling speed - 200 rpm, and milling balls size - 5 mm in diameter).