Abstract
This study evaluated the effect of heating on the physicochemical properties and surface changes of tricalcium silicate sealers. Three tricalcium silicate root canal sealers (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer), and one epoxy resin-based sealer (AH Plus; control) were tested. The effect of heating on setting time (ST) and flowability were assessed according to ANSI/ADA 57 and ISO 6876 standards. Solubility and dimensional change (DC) of the set sealers were evaluated at 24 hours and after 30 days; the pH of the water used in the DC testing was also measured. Tests were repeated with heated sealers in an oven at 100 °C for 1 min. SEM and EDS analysis were performed. Data were analyzed using One-Way ANOVA and Tukey post-hoc tests (α=5%). Heating decreased the ST for AH Plus and EndoSequence (p<0.05). Heating reduced flowability (p<0.05) and increased pH for AH Plus (p<0.05). The solubility of Bio-C (dried specimens) was not in accordance with the ANSI/ADA standard. The solubility of EndoSequence was significantly higher (p<0.05) when it was heated and dried after 30 days. DC of Bio-C (24 h and 30 days), BioRoot-RCS (30 days) and AH Plus (24 h and 30 days) were not in accordance with the standards. SEM and EDS analysis showed significant changes in sealer microstructure after heating. In conclusion, heating decreased the ST and increased the solubility of EndoSequence BC sealer. No significant changes in flowability, DC, and pH were identified for all three tricalcium silicate sealers after heat application. However, all sealers had significant surface changes.