Abstract
In this study, the effect of boric acid (H(3)BO(3)) on fiber-reinforced layered composites was investigated. Glass fiber-reinforced epoxy composites were used, and the effects of boric acid on thermal and mechanical properties were investigated. For this purpose, composite plates were manufactured by adding boric acid (BA) to the epoxy in different ratios (0, 0.5, 1, and 1.5% by weight). Tensile tests, compression tests, and shear tests were performed to determine the mechanical properties of these plates, and DSC, TGA, and DMA analyses were performed to determine their thermal properties. SEM and EDS analyses were performed on the specimens to examine their morphologies. Furthermore, examinations were conducted on how BA affected the specimens' failure behavior. In the study, it was found that, except for the compressive strength, the mechanical properties were improved by the added BA. The highest tensile strength, shear strength, modulus of elasticity, shear modulus, and Poisson's ratio were obtained from 0.5% BA-added specimens and were 24.78%, 8.75%, 25.13%, 11.24%, and 12.5% higher than the values obtained from 0% BA-added specimens, respectively. The highest loss and storage modulus were obtained from 0% and 0.5% BA-added specimens, respectively. The specimens' glass transition temperatures were decreased by the addition of BA; the specimen with a 1% addition of BA had the lowest value. Furthermore, interlayer delamination and fiber/matrix failure were observed in all BA-added specimens.