Abstract
Fire barriers are used to reduce the risk of fire spreading over façades. External thermal insulation composite systems consist of mineral wool strips embedded in a layer of another thermal insulation material. A system configured in this manner, beyond standard solutions, can be more susceptible to environmental factors. In this study, an expanded polystyrene-based system with a mineral wool fire barrier was subjected to weathering conditions. In view of climate change, nonconventional long-lasting exposure simulating the effects of intensive atmospheric factors was applied. Two exposure sequences were used, each covering 80 cycles of heating and wetting, five cycles of heating and cooling, and 30 cycles of wetting, freezing, and thawing. Significant changes were observed in the first sequence. The second sequence caused rendering system cracks wider than 0.2 mm. This indicated a loss of watertightness. A new approach of 3D scanning with inspection analysis was used to assess the deformations. It showed deformation amounted to 0.7 mm within the MW strip. The methods used previously did not allow this level of deformation to be recorded.