Abstract
In this study, we optimized the traditional composition of AISI 8630 steel and evaluated its corrosion resistance through a series of tests. We conducted corrosion tests in a 3.5% NaCl solution and performed a 720 h fixed-load tensile test in accordance with the NACE TM-0177-2016 standard to assess sulfide stress corrosion cracking (SSCC). To analyze the corrosion products and the structure of the corrosion film, we employed X-ray diffraction and transmission electron microscopy. The corrosion rate, characteristics of the corrosion products, structure of the corrosion film, and corrosion resistance mechanism of the material were investigated. The results indicate that the optimized AISI 8630 material demonstrates excellent corrosion resistance. After 720 h of exposure, the primary corrosion products were identified as chromium oxide, copper sulfide, iron oxide, and iron-nickel sulfide. The corrosion film exhibited a three-layer structure: the innermost layer with a thickness of 200-300 nm contained higher concentrations of alloying elements and formed a dense, cohesive rust layer that hindered the diffusion of oxygen and chloride ions, thus enhancing corrosion resistance. The middle layer was thicker and less rich in alloying elements, while the outer layer, approximately 300-400 nm thick, was relatively loose.