Abstract
The occurrence of adiabatic shear bands, as an instability phenomenon, is viewed as a precursor to failure caused by instability at high strain rates. Metastable β titanium alloys are extensively utilized due to their excellent mechanical properties, which are often subjected to high strain rate loads in service conditions. Understanding and studying their adiabatic shear instability behavior is thus crucial for preventing catastrophic failure and enhancing material performance. In this study via detailed microstructural analyses in the adiabatic shear region of a Ti-10V-2Fe-3Al alloy subjected to high strain rates, it was observed that α″ martensitic transformation and nano-twinning plus β-to-α phase transformation with α″ martensite as an intermediate phase occurred, in addition to substantial fine grains. The grain refinement mechanisms were mainly related to dynamic recovery dominated by dislocation migration alongside severe plastic deformation.