Abstract
PURPOSE: The aim of the in vitro study was to compare the internal merge and marginal perfection of polyetheretherketone (PEEK) and polyetherketoneketone (PEKK) crowns under a stereomicroscope. METHODS: All-ceramic preparation is done on the maxillary first premolar which is mounted on the wax block which was scanned using 3Shape scanner and duplicated into 30 acrylic CAD/CAM dies (n = 15) for the placement of PEEK and PEKK crowns. The YENADENT milling system was used to fabricate 15 samples from Group A PEEK crowns and to fabricate 15 samples from Group B PEKK crowns. According to the manufacturer's instructions, an equal amount of the dual-cure resin luting agent (Rely X U200 Self-Adhesive resin, 3M, Germany) was dispensed on the mixing pad before being mixed with cement and painted on the internal surfaces of the copings with the finger pressure crowns which were luted. The values were then analyzed using one-way ANOVA (post hoc) followed by Dunnett's t-test. RESULTS: Among those two groups, PEEK group materials showed the lowest mean value of (28.73.3 ± 4.01) for marginal fit and (26.72 ± 2.53) for internal gap, whereas PEKK group showed a mean value of (32.85 ± 4.63) and (33.06 ± 4.14), respectively. CONCLUSION: Among these two groups, comparatively less marginal fit and internal adaptation is seen in PEKK when compared to the PEEK crowns. While the marginal fit and internal adaptation of both PEEK and PEKK copings were in acceptable clinical range.