Abstract
This study validates the attributes of the mineral carbonation process employing circulating fluidized bed combustion (CFBC) ash, which is generated from thermal power plants, as a medium for carbon storage. Furthermore, an examination was conducted on the properties of construction materials produced through the recycling of carbonated circulating fluidized bed combustion (CFBC) ash. The carbonation characteristics of circulating fluidized bed combustion (CFBC) ash were investigated by analyzing the impact of CO(2) flow rate and solid content. Experiments were conducted to investigate the use of it as a concrete admixture by replacing cement at varying percentages ranging from 0% to 20% by weight. The stability and setting time were subsequently measured. To produce foam concrete, specimens were fabricated by substituting 0 to 30 wt% of the cement. Characteristics of the unhardened slurry, such as density, flow, and settlement depth, were measured, while characteristics after hardening, including density, compressive strength, and thermal conductivity, were also assessed. The findings of our research study validated that the carbonation rate of CFBC ash in the slurry exhibited distinct characteristics compared to the reaction in the solid-gas system. Manufactured carbonated circulating fluidized bed combustion (CFBC) ash, when used as a recycled concrete mixture, improved the initial strength of cement mortar by 5 to 12% based on the 7-day strength. In addition, it replaced 25 wt% of cement in the production of foam concrete, showing a density of 0.58 g/cm(3), and the 28-day strength was 2.1 MPa, meeting the density standard of 0.6 grade foam concrete.