Abstract
Low-grade limestone (LGL) is not used to produce cement clinker, but this leftover material in cement quarries increases the water demand when used as a filler in concrete production. In this study, the effect of six commercial superplasticizers on the performance of cement mixes containing 35% LGL and 2% gypsum was investigated. The optimal doses of these superplasticizers were found in a range of different water/binder (w/b) ratios by conducting several Marsh cone and mini-slump tests. The addition of a superplasticizer with a higher active solid content produced a maximum cement flow, regardless of the w/b ratios. The LGL-based mortar samples admixed with this superplasticizer obtained a maximum compressive strength of about 36 MPa at the end of 28 days. SEM and XRD results showed the formation of a new calcium-rich mineral in their microstructure. These findings highlight the impact of the type and properties of superplasticizers on the performance of concrete mixes containing LGL as a supplementary cementitious material.