Abstract
Considering the significant health risks posed by hard chrome plating during its application, thermally sprayed Cr(3)C(2)-NiCr cermet coatings represent a suitable alternative. Incorporating hexagonal boron nitride (hBN) as a dry lubricant into the feedstock powder can further enhance wear resistance and thermal conductivity, crucial for preventing premature failure caused by inadequate lubrication. In this study, the mass fraction of hBN was varied between 0 and 15 wt.% to assess its influence on the tribological performance of the coatings using pin-on-disk tests. The coating's hardness was measured via the Vickers method, and its cracking tendency at the coating/substrate interface was evaluated. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were employed to analyze the microstructure and phase composition, while thermal diffusivity was determined using the laser flash method. The findings revealed that the inclusion of hBN, at concentrations of up to 10 wt.%, leads to an improvement in thermal diffusivity and a reduction in the coefficient of friction. However, exceeding this threshold leads to a decrease in hardness and increased crack formation tendency, highlighting the trade-off between frictional and mechanical properties.