Abstract
In the present study, in-situ observation of Hot Isostatic Pressure (HIP) procedure of laser powder bed fusion manufactured Ti-6Al-4V parts was performed to quantitatively estimate the densification rate of the material and the influence of the defect initial size and shape on such rate. The observations were performed in-situ using the Ultrafast Tomography Paris-Edinburgh Cell and the combination of fast phase-contrast synchrotron X-ray tomography and energy dispersive diffraction. With this strategy, we could quantify how the effectiveness of HIP depends on the characteristics of a defect. Smaller defects showed a higher densification rate, while the defect shape did not have significant effect on such rate.