Abstract
Thermal barrier coatings (TBCs) are critical for protecting hot-section components in gas turbines and aero-engines. Traditional yttria-stabilized zirconia (YSZ) coatings are prone to phase transformation and sintering-induced failure at elevated temperatures. This study fabricated CeScYSZ (4 mol% CeO(2) and 6 mol% Sc(2)O(3) co-doped YSZ)/NiCrAlY TBCs using atmospheric plasma spraying (APS). A five-factor, four-level orthogonal experimental design was employed to optimize spraying parameters, investigating the influence of powder feed rate, spray distance, current, hydrogen flow rate and primary gas flow rate on the coating's microstructure and mechanical properties. The resistance to calcium-magnesium-alumino-silicate (CMAS) corrosion was compared between CeScYSZ and YSZ coatings. The results indicate that the optimal parameters are a spray distance of 100 mm, current of 500 A, argon flow rate of 30 L/min, hydrogen flow rate of 6 L/min, and powder feed rate of 45 g/min. Coatings produced under these conditions exhibited moderate porosity and excellent bonding strength. After exposure to CMAS corrosion at 1300 °C for 2 h, the CeScYSZ coating demonstrated significantly superior corrosion resistance compared to YSZ. This enhancement is attributed to the formation of a CaZrO(3) physical barrier and the synergistic effect of Ce and Sc in suppressing deleterious phase transformations. This study provides an experimental basis for the preparation and application of high-performance TBCs.