Abstract
Cement production requires considerable energy and natural resources, severely impacting the environment due to harmful gas emissions. Coal bottom ash (CBA) and coal boiler slag (CBS), byproducts of coal-fired powerplants having pozzolanic properties, can be mechanically ground and replace cement in concrete, which reduces waste in landfills, preserves natural resources, and reduces health hazards. This study was performed to determine the optimum cement replacement amount of ground CBA (GCBA) and ground CBS (GCBS) in concrete, which was 10% for GCBA and 5% for GCBS. GCBA-based concrete exhibited superior tensile strength, modulus of elasticity, and durability compared to the control. In the Rapid Chloride Penetration Test, 10% GCBA concrete resulted in 2026 coulombs at 56 days, compared to 3405 coulombs for the control, indicating more resistance to chloride penetration. Incorporating 2.5% nanoclay in GCBA-based concrete increased the optimum GCBA content by 5%, and the compressive strength of 15% GCBA concrete increased by 4 MPa. The mortar consisting of the finest GCBA(L1) having Blaine fineness of 3072 g/cm(2) yielded the highest compressive strength (32.7 MPa). The study discovered that the compressive strength of GCBA and GCBS-based mortars increases with fineness, and meeting the recommended fineness limit in ASTM C618 enhances concrete or mortar properties.