Abstract
This study investigated the self-healing properties of PA6/COC blends, in particular, the impact of three compatibilizers on the rheological, microstructural, and thermomechanical properties. Dynamic rheological analysis revealed that ethylene glycidyl methacrylate (E-GMA) played a crucial role in reducing interfacial tension and promoting PA6 chain entanglement with COC domains. Mechanical tests showed that poly(ethylene)-graft-maleic anhydride (PE-g-MAH) and polyolefin elastomer-graft-maleic anhydride (POE-g-MAH) compatibilizers enhanced elongation at break, while E-GMA had a milder effect. A thermal healing process at 140 °C for 1 h was carried out on specimens broken in fracture toughness tests, performed under quasi-static and impact conditions, and healing efficiency (HE) was evaluated as the ratio of critical stress intensity factors of healed and virgin samples. All the compatibilizers increased HE, especially E-GMA, achieving 28.5% and 68% in quasi-static and impact conditions, respectively. SEM images of specimens tested in quasi-static conditions showed that all the compatibilizers induced PA6 plasticization and crack corrugation, thus hindering COC flow in the crack zone. Conversely, under impact conditions, E-GMA led to the formation of brittle fractures with planar surfaces, promoting COC flow and thus higher HE values. This study demonstrated that compatibilizers, loading mode, and fracture surface morphologies strongly influenced self-healing performance.