Abstract
Although various degradable gel materials have been developed for temporary plugging in oil fields, they often degrade too quickly in high-temperature environments. To address this issue, an unstable crosslinker was synthesized to prepare a high-temperature degradable gel. This gel does not degrade excessively fast at high temperatures. Temperature and crosslinker concentration are the primary factors influencing gel degradation time, followed by monomer and initiator concentrations. Increased temperature and decreased crosslinker concentration both reduce degradation time, which can be adjusted within the range of 90-130 °C by varying the crosslinker concentration. The molecular structure and thermal stability of the degradable gel were analyzed using FTIR, (13)C NMR, and TG. Furthermore, the viscoelastic properties, compressive performance, plugging performance, and core damage performance of the gel were evaluated. Within the test range of 0.1-1000 Pa, the storage modulus is higher than the loss modulus. The gel prepared at 130 °C exhibited a compressive stress of 0.25 MPa at 50% strain. The plugging pressure of the gel in sand-filled tubes with varying permeabilities (538.2-2794.1 mD) exceeded 15 MPa while maintaining a core damage rate below 5%. SEM analysis indicated that the degradation mechanism of the gel may involve the collapse of its three-dimensional network structure due to the hydrolysis of amide groups in the crosslinker. The viscosity of the degradation liquid was below 11 mPa·s, enabling it to be brought back to the surface with the formation fluid without the need for further breaking operations.