Abstract
This paper presents the experimental results of a study evaluating the mechanical and fatigue performance of welded Fe-Mn-Si SMA. For the experimental study, welded and welded-and-heat-treated Fe-Mn-Si SMA specimens were fabricated, and fatigue tests were performed at various stress amplitudes. In addition, direct tensile tests and recovery stress tests were also performed to evaluate the material properties of Fe-Mn-Si SMAs. The elastic modulus, yield strength, and tensile strength of the welded specimens were reduced by 35.4%, 12.1%, and 8.6%, respectively, compared to the values of the non-welded specimens. On the other hand, the elastic modulus, yield strength, and tensile strength of the welded-and-heat-treated Fe-Mn-Si SMA specimens were increased by 18.6%, 4.9%, and 1.3%, respectively, compared to the values of the welded specimens. Both welded and welded-and-heat-treated Fe-Mn-Si SMAs failed at lower cycles than the conventional Fe-Mn-Si SMAs at the same stress amplitude. High-cycle fatigue failure, characterized by cycles exceeding 10(4), typically occurs at relatively low stress levels within the elastic region, whereas low-cycle fatigue failure, generally occurring within cycles below 10(4), involves high stress levels that encompass both elastic and plastic deformation. Regardless of the welding condition, the stress amplitude at which Fe-Mn-Si SMA transitions from high-cycle to low-cycle failure exceeded the yield strength.