Abstract
In this study, the decomposition of a martensite/austenite (M/A) microconstituent in bainitic steels was analyzed using differential scanning calorimetry (DSC) data in conjunction with Kissinger's and Johnson-Mehl-Avrami-Kolmogorov (JMAK)'s formulas. In bainitic steel subjected to austempering heat treatment, the presence of an M/A microstructure adversely affects the mechanical properties. According to the kinetic equations derived, it is observed that after tempering the sample at 600 °C for 4000 s, the generation of each phase reaches its maximum. The SEM images taken before and after tempering reveal extensive decomposition of the M/A constituent in the microstructure. The proportion of the M/A microstructure decreased significantly from about 10% before tempering to less than 1% after. Additionally, the content of residual austenite also reduced nearly to zero. These observations are consistent with the predictions of the kinetic equations.