Abstract
Additive manufacturing (AM) of nickel-based superalloys is of high interest for application in complex hot end parts. However, it has been widely suggested that the microstructure-properties of the additive manufacturing processed superalloys are not yet fully clear. In this study, the GTD222, an important superalloy for high-temperature hot-end part, were prepared using selective laser melting and then subjected to heat treatment. The microstructure evolution of the GTD222 was investigated and the mechanical properties of heat treated GTD222 were tested. The results have shown that the grain size of the heat treated GTD222 was close to its as-built counterparts. Meanwhile, a large amount of γ' and nano-scaled carbides were precipitated in the heat treated GTD222. The microstructure characteristics implied that the higher strength of the heat treated GTD222 can be attributed to the γ' and nano-scaled carbides. This study provides essential microstructure and mechanical properties information for optimizing the heat treatment process of the AM processed GTD222.