Aim
This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. Materials and method: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope.
Conclusions
The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer. Objetivo: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. Resultados: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levou a uma menor permeabilidade dentinária e a mais irregularidades na superfície da camada adesiva.
Results
There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. Conclusions: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer. Objetivo: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. Resultados: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levou a uma menor permeabilidade dentinária e a mais irregularidades na superfície da camada adesiva.