Conclusion
A combined mechanism of lattice/hole diffusion-dissolution governed the release of everolimus with the activation energies of 5.409 kJ/mol and 4.936 kJ/mol for the first 24 hr and diffusion coefficients 6.06×10-10 and 3.64×10-11cm2/s for the 50th to 100th days. Prolonged suppression of hyperplasia within the smooth muscle cells by hybrid stent insertion could bring about the cessation of restenosis.
Methods
Therefore, more research has been needed to legitimize the replacement of current stents with Mg-based stents. UV-Vis spectrophotometer, scanning electron microscope (SEM), X-ray diffraction (XRD), pH measurement, H&sub2; evolution, and corrosion tests determined the change in hybrid properties and drug release rate.
Results
The effect of Mg degradation on drug release from poly-L-lactide (PLLA) specimen was much higher than that of the L605/PLLA sample. Hydrogen evolution caused by magnesium degradation compelled everolimus out without significant PLLA decomposition during the first 100 days, while formation of Mg(OH)2 caused the PLLA to deform and crack.