Conclusions
The coating method of β-TCP with PDLLA revealed a potential strategy to increase the mechanical strength of porous ceramic materials while collagen can enhance cell migration.
Methods
β-TCP powder was obtained by reactive milling and then characterized by X-ray diffraction and scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS). β-TCP scaffolds were obtained by replica method, in which polyurethane foams are immersed in β-TCP suspension and thereafter submitted to a thermal treatment to remove the polyurethane and sinter the ceramic. Type-I collagen or PDLLA were used to coat the β-TCP scaffolds by dip-coating method. Scaffolds were separated in four groups depending on the coating material: noncoated (Group A), double immersion in collagen (Group B), double immersion in PDLLA (Group C), and ten immersions in PDLLA (Group D). Samples were characterized by compressive tests and SEM/EDS. Data were statistically analyzed through two-way ANOVA (p = 0.05).
Results
Chemical and microscopic analyses revealed proper morphology and chemical composition of powder particles and scaffolds with or without polymeric coatings. Scaffolds coated with PDLLA showed higher compressive strength (0.11 ± 0.054 MPa) than those of collagen (0.022 ± 0.012 MPa) or noncoated groups (0.024 ± 0.012 MPa). Conclusions: The coating method of β-TCP with PDLLA revealed a potential strategy to increase the mechanical strength of porous ceramic materials while collagen can enhance cell migration.