Abstract
Silver nanoparticle-modified graphene oxide (Ag/GO) was reliably prepared by using sodium borohydride (NaBH4) in the presence of citric acid capping agent via a simple wet chemistry method. This rapidly formed Ag/GO composite exhibited good dispersity in a solution containing hydrophilic polyacrylonitrile (PAN). Subsequent electrospinning of this precursor solution resulted in the successful formation of nanofibers without any notable defects. The Ag/GO-incorporated PAN nanofibers showed thinner fiber strands (544 ± 82 nm) compared to those of GO-PAN (688 ± 177 nm) and bare-PAN (656 ± 59 nm). Subsequent thermal treatment of nanofibers resulted in the preparation of thin membranes to possess the desired pore property and outstanding wettability. The Ag/GO-PAN nanofiber membrane also showed 30% higher water flux value (390 LMH) than that of bare-PAN (300 LMH) for possible microfiltration (MF) application. In addition, the resulting Ag/GO-PAN nanofiber membrane exhibited antibacterial activity against Escherichia coli (Gram-negative) and Staphylococcus aureus (Gram-positive). Furthermore, this composite membrane exhibited outstanding anti-fouling property compared to the GO-PAN nanofiber membrane in the wastewater treatment. Therefore, the simple modification strategy allows for the effective formation of Ag/GO composite as a filler that can be reliably incorporated into polymer nanofiber membranes to possess improved overall properties for wastewater treatment applications.