Abstract
A novel approach for investigating the formation of solid electrolyte interphase (SEI) in Na-ion batteries (NIB) through the coupling of in situ liquid electrochemical transmission electron microscopy (ec-TEM) and gas-chromatography mass-spectrometry (GC/MS) is proposed. To optimize this coupling, experiments are conducted on the sodiation of hard carbon materials (HC) using two setups: in situ ec-TEM holder and ex situ setup. Electrolyte (NP30) is intentionally degraded using cyclic voltammetry (CV), and the recovered liquid product is analyzed using GC/MS. Solid product (µ-chip) is analyzed using TEM techniques in a post-mortem analysis. The ex situ experiments served as a reference to for insertion of Na+ ions in the HC, SEI size (389 nm), SEI composition (P, Na, F, and O), and Na plating. The in situ TEM analysis reveals a cyclability limitation, this issue appears to be caused by the plating of Na in the form of a "foam" structure, resulting from the gas release during the reaction of Na with DMC/EC electrolyte. The foam structure, subsequently transformes into a second SEI, is electrochemically inactive and reduces the cyclability of the battery. Overall, the results demonstrate the powerful synergy achieved by coupling in situ ec-TEM and GC/MS techniques.